The EZ175 is a two component, polyamide cured, the metal-rich zinc epoxy primer for steel in severely corrosive environment to provide long-lasting protection and excellent resistance to mechanical wear performance as an excellent container primer has been recognized by the British Lloyd's Register (LR) and Constant, Laboratories Inc. in accordance with the norms of the U.S. Food and Drug Administration (FDA) 175.300 section specification, it can be used in fresh water tanks and re-coated with a suitable finish. 
 As a corrosive environment and subjected to mechanical wear of steel long-lasting protection primer. As from blasting to the final top coat shop primer for corrosion protection. 

 Drying time 
 Temperature of 5 ℃ / 41 ℉ to 20 ℃ / 68 ℉ to 30 ° C / 86 ° F 
 Dry to touch 50 Min, 20 Min, 10 Min. 
 Hard dry 12 Hours, 6 Hours, 4 Hours, 

 Volume solids Approx. By 48% (Determined by the ISO 3 233) 
 Approximately 48% (determination according to ISO 3233) 
 Theoretical spreading rate of 12.0 square meters / L in. 40? Dry film thickness on a smooth surface. 
 On a smooth surface, dry film thickness of 40?, Theoretical spreading rate of 12.0 m / L. 
 The proportion of Approx. 2.60 for Mixture. Of the Base and Curing the agent. 
 About 2.60 (main agent and curing agent mixture) 

 Galvany Shopprimer IZ182 (C) 
 Own curing inorganic zinc primer. Liquid main agent and zinc powder mixture. 
 Galvany Shopprimer IZ182 (C) on cathodic corrosion protection of the substrate after construction of the substrate can be excellent welding performance. 
 Paint is dry before touching it. 
 As shop primer used in shipbuilding, oil tank, steel and other more cost effective than traditional shop primer to avoid contact with the acid-base. 
 Drying the Time 
 (At 65% RH) Substrate temperature 
 Temperature of 5 ℃ / 41 ℉ to 20 ℃ / 68 ℉ to 30 ° C / 86 ° F 
 Drying time 
 Dry to touch 45 Min, 10 Min, 5 Min. 
 Hard dry 25 Hours, 10 Hours, 5 Hours, 
 Volume solids Approx. 30% 
 About 30% (according to ISO 3 233) 
 Theoretical spreading rate of 20.0 m / L in 15?, Dry film thickness on a smooth surface 
 On a smooth surface, dry film thickness of 15?, Theoretical spreading rate of 20.0 m / L. 
 The proportion of Approx. Approx 1.2 for Mixture. The filler of the Base and Zinc- 
 About 1.2 (main agent and zinc Tim filling the mixture of agent)