EH6270 (H) is a two component, polyamide cured epoxy resin as the base material, thick paste coating, it has good water resistance and excellent corrosion resistance as a thick slurry primer or intermediate coat used in the bridge and steel on steel exposed to the outside area is recommended to use a polyurethane finish. 

 Drying time Substrate temperature 
 Substrate temperature of 5 ℃ / 41 ℉ to 20 ℃ / 68 ℉ to 30 ° C / 86 ° F 
 Dry to touch 18 Hours, 4 Hours, 3 Hours, 
 Hard dry 72 Hours, 24 Hours, 20 Hours, 

 Volume of the solid content Approx. To 70% (Determined by the ISO 3 233) 
 Approximately 70% (determination according to ISO 3233) 
 Theoretical spreading rate of 7.0 m / L in. 100? Dry film thickness on a smooth surface. 
 On a smooth surface, dry film thickness of 100? Theoretical spreading rate of 7.0 m / L. 
 The proportion of Approx. 1.45 for Mixture. Of the Base and Curing the agent. 
 About 1.45 (main agent and curing agent mixture) 


 ET5745 is a two-component thick paste, high weather resistance finish epoxy resin as the base material, it has good weather resistance and color retention as a corrosive marine and industrial environment, internal and external steel finish. anti-corrosion coatings for open-air parts requiring good color retention and weather resistance, such as the upper deck of the ship outside the deckhouse. 

 Drying time Substrate temperature 
 Substrate temperature of 5 ℃ / 41 ℉ to 20 ℃ / 68 ℉ to 30 ° C / 86 ° F 
 Dry to touch 10 Hours, 2 Hours, 2 Hours, 
 Hard dry 48 Hours, 24 Hours, 20 Hours, 

 The volume of the solid content Approx. By 58% (Determined by the ISO 3 233) 
 Approximately 58% (determination according to ISO 3233) 
 Theoretical spreading rate of 5.8 m / L, in. 100? Dry film thickness on a smooth surface. 
 On a smooth surface, dry film thickness of 100?, Theoretical spreading rate of 5.8 m / L. 
 The proportion of Approx. 1.30 for Mixture. Of the Base and Curing the agent. 
 About 1.30 (main agent and curing agent mixture)