Korepox EH2350 is a two-component epoxy resin substrate surface dual-use wear-resistant coatings with good resistance to sea water, crude oil, fuel and wear resistance coatings as a surface tolerance construction to simply remove the old and the new steel rust, curing it in the low temperature to -18 ° C / -0.4 ° F conditions. meet the VOC requirements of the high solid coatings. 
 As a ballast tank corrosion control coatings British Register of Shipping (LR) and Germanischer Lloyd (GL) certification as a fire-resistant paint Det Norske Veritas (DNV, the CE Marking) United Kingdom Register (LR) and the Korean shipping (KR) certification of the Class Society. certification of the British health authorities contamination of grain material. MARINTEK / DNV certification for good ballast tank coatings. fully comply with NORSOK M-501, rev 4, System No. 7 provisions. certified for compliance with IMO -of PSPC regulations ballast tank corrosion control coatings as corrosion and wear-resistant coatings to protect long-term severely corroded area of ??steel materials, such as underwater ship hull plate area between the waterline and freeboard, ship appearance , ballast tanks, cargo tanks, etc. as a tank coating used to ship crude oil tanks, fuel tanks and crude oil pipeline wall. can also be applied to marine buildings, factories, bridges and other steel structures. 
 Drying time 
 Substrate temperature of 5 ℃ / 41 ℉ to 20 ℃ / 68 ℉ to 30 ° C / 86 ° F 

 Dry to touch 8 Hours, 1 Hour 30 Min. 

 Hard dry in 16 Hours, 3 Hours, 2 Hours, 

 Solids by the Volume 
 Volume solids Approx. To 80% (Determined by the ISO 3 233) 
 About 80% (according to ISO 3 233) 

 Theoretical Spreading Rate 
 Theoretical spreading rate of 6.40 square meters / L in. 125? Dry film thickness on a smooth surface. 
 Smooth surface, dry film thickness of 125? Theoretical spreading rate of 6.40 m / L. 

 Specific Gravity, 
 The proportion of Approx. 1.50 for Mixture. Of the Base and Curing the agent. 
 After mixing, approximately 1.50